5457 Aluminum vs. EN 1.0214 Steel
5457 aluminum belongs to the aluminum alloys classification, while EN 1.0214 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5457 aluminum and the bottom bar is EN 1.0214 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 32 to 55 | |
| 97 to 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 190 |
| Elongation at Break, % | 6.0 to 22 | |
| 12 to 31 |
| Fatigue Strength, MPa | 55 to 98 | |
| 160 to 250 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 73 |
| Shear Strength, MPa | 85 to 130 | |
| 250 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 130 to 210 | |
| 330 to 460 |
| Tensile Strength: Yield (Proof), MPa | 50 to 190 | |
| 210 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 660 | |
| 1470 |
| Melting Onset (Solidus), °C | 630 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 180 | |
| 53 |
| Thermal Expansion, µm/m-K | 24 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 46 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 1.8 |
| Density, g/cm3 | 2.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 160 | |
| 18 |
| Embodied Water, L/kg | 1190 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 23 | |
| 34 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 18 to 250 | |
| 120 to 340 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 12 to 16 |
| Strength to Weight: Bending, points | 21 to 28 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 72 | |
| 14 |
| Thermal Shock Resistance, points | 5.7 to 9.0 | |
| 11 to 14 |
Alloy Composition
| Aluminum (Al), % | 97.8 to 99.05 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 | |
| 0.080 to 0.12 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 99.17 to 99.6 |
| Magnesium (Mg), % | 0.8 to 1.2 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.45 | |
| 0.3 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 |