5652 Aluminum vs. 5251 Aluminum
Both 5652 aluminum and 5251 aluminum are aluminum alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is 5652 aluminum and the bottom bar is 5251 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 47 to 77 | |
| 44 to 79 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 6.8 to 25 | |
| 2.0 to 19 |
| Fatigue Strength, MPa | 60 to 140 | |
| 59 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 110 to 170 | |
| 110 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 290 | |
| 180 to 280 |
| Tensile Strength: Yield (Proof), MPa | 74 to 260 | |
| 67 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 610 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 150 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 8.5 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 39 | |
| 5.4 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 40 to 480 | |
| 33 to 450 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 20 to 30 | |
| 18 to 29 |
| Strength to Weight: Bending, points | 27 to 36 | |
| 26 to 35 |
| Thermal Diffusivity, mm2/s | 57 | |
| 61 |
| Thermal Shock Resistance, points | 8.4 to 13 | |
| 7.9 to 13 |
Alloy Composition
| Aluminum (Al), % | 95.8 to 97.7 | |
| 95.5 to 98.2 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 to 0.15 |
| Copper (Cu), % | 0 to 0.040 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 1.7 to 2.4 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.1 to 0.5 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |