5652 Aluminum vs. QE22A Magnesium
5652 aluminum belongs to the aluminum alloys classification, while QE22A magnesium belongs to the magnesium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is 5652 aluminum and the bottom bar is QE22A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 47 to 77 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 44 |
| Elongation at Break, % | 6.8 to 25 | |
| 2.4 |
| Fatigue Strength, MPa | 60 to 140 | |
| 110 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 17 |
| Shear Strength, MPa | 110 to 170 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 290 | |
| 250 |
| Tensile Strength: Yield (Proof), MPa | 74 to 260 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 250 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 970 |
| Thermal Conductivity, W/m-K | 140 | |
| 110 |
| Thermal Expansion, µm/m-K | 24 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 120 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 2.0 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 27 |
| Embodied Energy, MJ/kg | 150 | |
| 220 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 39 | |
| 5.5 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 40 to 480 | |
| 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 60 |
| Strength to Weight: Axial, points | 20 to 30 | |
| 36 |
| Strength to Weight: Bending, points | 27 to 36 | |
| 46 |
| Thermal Diffusivity, mm2/s | 57 | |
| 59 |
| Thermal Shock Resistance, points | 8.4 to 13 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 95.8 to 97.7 | |
| 0 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.040 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 93.1 to 95.8 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Silver (Ag), % | 0 | |
| 2.0 to 3.0 |
| Unspecified Rare Earths, % | 0 | |
| 1.8 to 2.5 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |