5652 Aluminum vs. R60705 Alloy
5652 aluminum belongs to the aluminum alloys classification, while R60705 alloy belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5652 aluminum and the bottom bar is R60705 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 98 |
| Elongation at Break, % | 6.8 to 25 | |
| 18 |
| Fatigue Strength, MPa | 60 to 140 | |
| 290 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 26 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 290 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 74 to 260 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 270 |
| Thermal Conductivity, W/m-K | 140 | |
| 17 |
| Thermal Expansion, µm/m-K | 24 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 6.7 |
| Embodied Water, L/kg | 1190 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 39 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 40 to 480 | |
| 950 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 51 | |
| 23 |
| Strength to Weight: Axial, points | 20 to 30 | |
| 22 |
| Strength to Weight: Bending, points | 27 to 36 | |
| 22 |
| Thermal Diffusivity, mm2/s | 57 | |
| 9.5 |
| Thermal Shock Resistance, points | 8.4 to 13 | |
| 63 |
Alloy Composition
| Aluminum (Al), % | 95.8 to 97.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.040 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 0 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91 to 98 |
| Residuals, % | 0 to 0.15 | |
| 0 |