60Pd-40Ag Alloy vs. EN 2.4878 Nickel
60Pd-40Ag alloy belongs to the otherwise unclassified metals classification, while EN 2.4878 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is EN 2.4878 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 100 | |
200 |
Elongation at Break, % | 1.1 to 28 | |
13 to 17 |
Poisson's Ratio | 0.38 | |
0.29 |
Shear Modulus, GPa | 37 | |
78 |
Shear Strength, MPa | 220 to 350 | |
750 to 760 |
Tensile Strength: Ultimate (UTS), MPa | 340 to 720 | |
1210 to 1250 |
Thermal Properties
Latent Heat of Fusion, J/g | 140 | |
330 |
Melting Completion (Liquidus), °C | 1360 | |
1370 |
Melting Onset (Solidus), °C | 1310 | |
1320 |
Specific Heat Capacity, J/kg-K | 240 | |
460 |
Thermal Conductivity, W/m-K | 29 | |
11 |
Thermal Expansion, µm/m-K | 15 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 11 | |
8.3 |
Common Calculations
Stiffness to Weight: Axial, points | 4.9 | |
13 |
Stiffness to Weight: Bending, points | 14 | |
24 |
Strength to Weight: Axial, points | 8.4 to 18 | |
41 to 42 |
Strength to Weight: Bending, points | 9.6 to 16 | |
31 |
Thermal Diffusivity, mm2/s | 11 | |
2.8 |
Thermal Shock Resistance, points | 16 to 34 | |
37 to 39 |
Alloy Composition
Aluminum (Al), % | 0 | |
1.2 to 1.6 |
Boron (B), % | 0 | |
0.010 to 0.015 |
Carbon (C), % | 0 | |
0.030 to 0.070 |
Chromium (Cr), % | 0 | |
23 to 25 |
Cobalt (Co), % | 0 | |
19 to 21 |
Copper (Cu), % | 0 to 0.1 | |
0 to 0.2 |
Iron (Fe), % | 0 | |
0 to 1.0 |
Manganese (Mn), % | 0 | |
0 to 0.5 |
Molybdenum (Mo), % | 0 | |
1.0 to 2.0 |
Nickel (Ni), % | 0 | |
43.6 to 52.2 |
Niobium (Nb), % | 0 | |
0.7 to 1.2 |
Palladium (Pd), % | 59.5 to 60.9 | |
0 |
Phosphorus (P), % | 0 | |
0 to 0.010 |
Silicon (Si), % | 0 | |
0 to 0.5 |
Silver (Ag), % | 39.1 to 40.5 | |
0 |
Sulfur (S), % | 0 | |
0 to 0.0070 |
Tantalum (Ta), % | 0 | |
0 to 0.050 |
Titanium (Ti), % | 0 | |
2.8 to 3.2 |
Zirconium (Zr), % | 0 | |
0.030 to 0.070 |
Residuals, % | 0 to 0.3 | |
0 |