60Pd-40Ag Alloy vs. G-CoCr28 Cobalt

60Pd-40Ag alloy belongs to the otherwise unclassified metals classification, while G-CoCr28 cobalt belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is G-CoCr28 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
210
Elongation at Break, % 1.1 to 28
6.7
Poisson's Ratio 0.38
0.28
Shear Modulus, GPa 37
83
Tensile Strength: Ultimate (UTS), MPa 340 to 720
560

Thermal Properties

Latent Heat of Fusion, J/g 140
320
Melting Completion (Liquidus), °C 1360
1330
Melting Onset (Solidus), °C 1310
1270
Specific Heat Capacity, J/kg-K 240
470
Thermal Conductivity, W/m-K 29
8.5
Thermal Expansion, µm/m-K 15
14

Otherwise Unclassified Properties

Density, g/cm3 11
8.1

Common Calculations

Stiffness to Weight: Axial, points 4.9
15
Stiffness to Weight: Bending, points 14
24
Strength to Weight: Axial, points 8.4 to 18
19
Strength to Weight: Bending, points 9.6 to 16
19
Thermal Diffusivity, mm2/s 11
2.2
Thermal Shock Resistance, points 16 to 34
14

Alloy Composition

Carbon (C), % 0
0.050 to 0.25
Chromium (Cr), % 0
27 to 30
Cobalt (Co), % 0
48 to 52
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0
9.7 to 24.5
Manganese (Mn), % 0
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 4.0
Niobium (Nb), % 0
0 to 0.5
Palladium (Pd), % 59.5 to 60.9
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0.5 to 1.5
Silver (Ag), % 39.1 to 40.5
0
Sulfur (S), % 0
0 to 0.030
Residuals, % 0 to 0.3
0