60Pd-40Ag Alloy vs. ZA-12
60Pd-40Ag alloy belongs to the otherwise unclassified metals classification, while ZA-12 belongs to the zinc alloys. There are 22 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 83 |
| Elongation at Break, % | 1.1 to 28 | |
| 1.6 to 5.3 |
| Knoop Hardness | 110 to 220 | |
| 110 to 130 |
| Poisson's Ratio | 0.38 | |
| 0.26 |
| Shear Modulus, GPa | 37 | |
| 33 |
| Shear Strength, MPa | 220 to 350 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 720 | |
| 260 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 120 |
| Melting Completion (Liquidus), °C | 1360 | |
| 430 |
| Melting Onset (Solidus), °C | 1310 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 450 |
| Thermal Conductivity, W/m-K | 29 | |
| 120 |
| Thermal Expansion, µm/m-K | 15 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.1 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 42 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 6.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.9 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 8.4 to 18 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 9.6 to 16 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 43 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 0 to 0.1 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 0 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Palladium (Pd), % | 59.5 to 60.9 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.060 |
| Silver (Ag), % | 39.1 to 40.5 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 87.1 to 89 |
| Residuals, % | 0 to 0.3 | |
| 0 |