6005 Aluminum vs. 336.0 Aluminum
Both 6005 aluminum and 336.0 aluminum are aluminum alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6005 aluminum and the bottom bar is 336.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 90 to 95 | |
| 110 to 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 75 |
| Elongation at Break, % | 9.5 to 17 | |
| 0.5 |
| Fatigue Strength, MPa | 55 to 95 | |
| 80 to 93 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 28 |
| Shear Strength, MPa | 120 to 210 | |
| 190 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 310 | |
| 250 to 320 |
| Tensile Strength: Yield (Proof), MPa | 100 to 280 | |
| 190 to 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 570 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 210 |
| Melting Completion (Liquidus), °C | 650 | |
| 570 |
| Melting Onset (Solidus), °C | 610 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 890 |
| Thermal Conductivity, W/m-K | 180 to 200 | |
| 120 |
| Thermal Expansion, µm/m-K | 23 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 54 | |
| 29 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 7.9 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1180 | |
| 1010 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 36 | |
| 1.1 to 1.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 77 to 550 | |
| 250 to 580 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Strength to Weight: Axial, points | 20 to 32 | |
| 25 to 32 |
| Strength to Weight: Bending, points | 28 to 38 | |
| 32 to 38 |
| Thermal Diffusivity, mm2/s | 74 to 83 | |
| 48 |
| Thermal Shock Resistance, points | 8.6 to 14 | |
| 12 to 16 |
Alloy Composition
| Aluminum (Al), % | 97.5 to 99 | |
| 79.1 to 85.8 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 0.5 to 1.5 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 1.2 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0.7 to 1.3 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 | |
| 2.0 to 3.0 |
| Silicon (Si), % | 0.6 to 0.9 | |
| 11 to 13 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.35 |
| Residuals, % | 0 to 0.15 | |
| 0 |