6013 Aluminum vs. AISI 204 Stainless Steel
6013 aluminum belongs to the aluminum alloys classification, while AISI 204 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6013 aluminum and the bottom bar is AISI 204 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 69 | |
200 |
Elongation at Break, % | 3.4 to 22 | |
23 to 39 |
Fatigue Strength, MPa | 98 to 140 | |
320 to 720 |
Poisson's Ratio | 0.33 | |
0.28 |
Shear Modulus, GPa | 26 | |
77 |
Shear Strength, MPa | 190 to 240 | |
500 to 700 |
Tensile Strength: Ultimate (UTS), MPa | 310 to 410 | |
730 to 1100 |
Tensile Strength: Yield (Proof), MPa | 170 to 350 | |
380 to 1080 |
Thermal Properties
Latent Heat of Fusion, J/g | 410 | |
280 |
Maximum Temperature: Mechanical, °C | 160 | |
850 |
Melting Completion (Liquidus), °C | 650 | |
1410 |
Melting Onset (Solidus), °C | 580 | |
1370 |
Specific Heat Capacity, J/kg-K | 900 | |
480 |
Thermal Conductivity, W/m-K | 150 | |
15 |
Thermal Expansion, µm/m-K | 23 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 38 | |
2.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
2.9 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 9.5 | |
10 |
Density, g/cm3 | 2.8 | |
7.7 |
Embodied Carbon, kg CO2/kg material | 8.3 | |
2.4 |
Embodied Energy, MJ/kg | 150 | |
35 |
Embodied Water, L/kg | 1170 | |
130 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 58 | |
240 to 250 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 900 | |
360 to 2940 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 49 | |
25 |
Strength to Weight: Axial, points | 31 to 41 | |
27 to 40 |
Strength to Weight: Bending, points | 37 to 44 | |
24 to 31 |
Thermal Diffusivity, mm2/s | 60 | |
4.1 |
Thermal Shock Resistance, points | 14 to 18 | |
16 to 24 |
Alloy Composition
Aluminum (Al), % | 94.8 to 97.8 | |
0 |
Carbon (C), % | 0 | |
0 to 0.030 |
Chromium (Cr), % | 0 to 0.1 | |
15 to 17 |
Copper (Cu), % | 0.6 to 1.1 | |
0 |
Iron (Fe), % | 0 to 0.5 | |
69.6 to 76.4 |
Magnesium (Mg), % | 0.8 to 1.2 | |
0 |
Manganese (Mn), % | 0.2 to 0.8 | |
7.0 to 9.0 |
Nickel (Ni), % | 0 | |
1.5 to 3.0 |
Nitrogen (N), % | 0 | |
0.15 to 0.3 |
Phosphorus (P), % | 0 | |
0 to 0.040 |
Silicon (Si), % | 0.6 to 1.0 | |
0 to 1.0 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Titanium (Ti), % | 0 to 0.1 | |
0 |
Zinc (Zn), % | 0 to 0.25 | |
0 |
Residuals, % | 0 to 0.15 | |
0 |