6014 Aluminum vs. 6065 Aluminum
Both 6014 aluminum and 6065 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 6014 aluminum and the bottom bar is 6065 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 68 |
| Elongation at Break, % | 9.1 to 17 | |
| 4.5 to 11 |
| Fatigue Strength, MPa | 43 to 79 | |
| 96 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 96 to 150 | |
| 190 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 260 | |
| 310 to 400 |
| Tensile Strength: Yield (Proof), MPa | 80 to 200 | |
| 270 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 620 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 890 |
| Thermal Conductivity, W/m-K | 200 | |
| 170 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 53 | |
| 43 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 8.4 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 | |
| 17 to 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 46 to 300 | |
| 540 to 1040 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 49 |
| Strength to Weight: Axial, points | 16 to 26 | |
| 31 to 40 |
| Strength to Weight: Bending, points | 24 to 33 | |
| 36 to 43 |
| Thermal Diffusivity, mm2/s | 83 | |
| 67 |
| Thermal Shock Resistance, points | 7.0 to 11 | |
| 14 to 18 |
Alloy Composition
| Aluminum (Al), % | 97.1 to 99.2 | |
| 94.4 to 98.2 |
| Bismuth (Bi), % | 0 | |
| 0.5 to 1.5 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 to 0.15 |
| Copper (Cu), % | 0 to 0.25 | |
| 0.15 to 0.4 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.4 to 0.8 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0.050 to 0.2 | |
| 0 to 0.15 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0.4 to 0.8 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Vanadium (V), % | 0.050 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |