6014 Aluminum vs. 6261 Aluminum
Both 6014 aluminum and 6261 aluminum are aluminum alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is 6014 aluminum and the bottom bar is 6261 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 69 |
| Elongation at Break, % | 9.1 to 17 | |
| 9.0 to 16 |
| Fatigue Strength, MPa | 43 to 79 | |
| 60 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 96 to 150 | |
| 90 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 260 | |
| 150 to 300 |
| Tensile Strength: Yield (Proof), MPa | 80 to 200 | |
| 100 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 620 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 200 | |
| 180 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 53 | |
| 48 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 160 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 8.3 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 | |
| 21 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 46 to 300 | |
| 77 to 500 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 16 to 26 | |
| 15 to 31 |
| Strength to Weight: Bending, points | 24 to 33 | |
| 23 to 37 |
| Thermal Diffusivity, mm2/s | 83 | |
| 75 |
| Thermal Shock Resistance, points | 7.0 to 11 | |
| 6.5 to 13 |
Alloy Composition
| Aluminum (Al), % | 97.1 to 99.2 | |
| 96.6 to 98.6 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.25 | |
| 0.15 to 0.4 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.4 to 0.8 | |
| 0.7 to 1.0 |
| Manganese (Mn), % | 0.050 to 0.2 | |
| 0.2 to 0.35 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0.4 to 0.7 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Vanadium (V), % | 0.050 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |