6018 Aluminum vs. AZ91E Magnesium
6018 aluminum belongs to the aluminum alloys classification, while AZ91E magnesium belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is 6018 aluminum and the bottom bar is AZ91E magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 46 |
| Elongation at Break, % | 9.0 to 9.1 | |
| 2.5 to 6.2 |
| Fatigue Strength, MPa | 85 to 89 | |
| 81 to 85 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 170 to 180 | |
| 89 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 300 | |
| 160 to 260 |
| Tensile Strength: Yield (Proof), MPa | 220 to 230 | |
| 96 to 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 640 | |
| 600 |
| Melting Onset (Solidus), °C | 570 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 990 |
| Thermal Conductivity, W/m-K | 170 | |
| 84 |
| Thermal Expansion, µm/m-K | 23 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 44 | |
| 10 to 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 52 to 60 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 12 |
| Density, g/cm3 | 2.9 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 22 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 25 | |
| 3.4 to 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 380 | |
| 100 to 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 48 | |
| 69 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 25 to 42 |
| Strength to Weight: Bending, points | 34 to 35 | |
| 37 to 53 |
| Thermal Diffusivity, mm2/s | 65 | |
| 49 |
| Thermal Shock Resistance, points | 13 | |
| 9.0 to 15 |
Alloy Composition
| Aluminum (Al), % | 93.1 to 97.8 | |
| 8.1 to 9.3 |
| Bismuth (Bi), % | 0.4 to 0.7 | |
| 0 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0.15 to 0.4 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.0050 |
| Lead (Pb), % | 0.4 to 1.2 | |
| 0 |
| Magnesium (Mg), % | 0.6 to 1.2 | |
| 88.8 to 91.3 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.17 to 0.35 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0010 |
| Silicon (Si), % | 0.5 to 1.2 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |