MakeItFrom.com
Menu (ESC)

6023 Aluminum vs. AWS BAg-13a

6023 aluminum belongs to the aluminum alloys classification, while AWS BAg-13a belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6023 aluminum and the bottom bar is AWS BAg-13a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
92
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 26
34
Tensile Strength: Ultimate (UTS), MPa 360
180

Thermal Properties

Latent Heat of Fusion, J/g 400
160
Melting Completion (Liquidus), °C 640
890
Melting Onset (Solidus), °C 580
770
Specific Heat Capacity, J/kg-K 890
300
Thermal Expansion, µm/m-K 23
19

Otherwise Unclassified Properties

Density, g/cm3 2.8
9.8
Embodied Carbon, kg CO2/kg material 8.3
54
Embodied Energy, MJ/kg 150
850

Common Calculations

Stiffness to Weight: Axial, points 14
5.2
Stiffness to Weight: Bending, points 49
15
Strength to Weight: Axial, points 35 to 36
5.1
Strength to Weight: Bending, points 40
7.2
Thermal Shock Resistance, points 16
7.5

Alloy Composition

Aluminum (Al), % 94 to 97.7
0
Bismuth (Bi), % 0.3 to 0.8
0
Copper (Cu), % 0.2 to 0.5
40.4 to 43.5
Iron (Fe), % 0 to 0.5
0
Magnesium (Mg), % 0.4 to 0.9
0
Manganese (Mn), % 0.2 to 0.6
0
Nickel (Ni), % 0
1.5 to 2.5
Silicon (Si), % 0.6 to 1.4
0
Silver (Ag), % 0
55 to 57
Tin (Sn), % 0.6 to 1.2
0
Residuals, % 0
0 to 0.15