6063 Aluminum vs. K94200 Alloy

6063 aluminum belongs to the aluminum alloys classification, while K94200 alloy belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6063 aluminum and the bottom bar is K94200 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
140
Elongation at Break, % 7.3 to 21
5.0 to 32
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
54
Shear Strength, MPa 70 to 190
330 to 410
Tensile Strength: Ultimate (UTS), MPa 110 to 300
500 to 710
Tensile Strength: Yield (Proof), MPa 49 to 270
270 to 650

Thermal Properties

Melting Onset (Solidus), °C 620
1440
Specific Heat Capacity, J/kg-K 900
500
Thermal Conductivity, W/m-K 190 to 220
15
Thermal Expansion, µm/m-K 23
5.0

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 49 to 58
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 160 to 190
3.0

Otherwise Unclassified Properties

Density, g/cm3 2.7
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 13 to 27
35 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 18 to 540
250 to 1460
Stiffness to Weight: Axial, points 14
9.8
Stiffness to Weight: Bending, points 50
21
Strength to Weight: Axial, points 11 to 31
17 to 24
Strength to Weight: Bending, points 18 to 37
17 to 22
Thermal Diffusivity, mm2/s 79 to 89
3.7
Thermal Shock Resistance, points 4.8 to 13
49 to 70