6063A Aluminum vs. 90-silver 10-nickel

6063A aluminum belongs to the aluminum alloys classification, while 90-silver 10-nickel belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6063A aluminum and the bottom bar is 90-silver 10-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
82
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 26
30
Tensile Strength: Ultimate (UTS), MPa 130 to 260
250 to 420

Thermal Properties

Latent Heat of Fusion, J/g 400
130
Melting Completion (Liquidus), °C 640
840
Melting Onset (Solidus), °C 620
960
Specific Heat Capacity, J/kg-K 900
260
Thermal Expansion, µm/m-K 23
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 49 to 54
90
Electrical Conductivity: Equal Weight (Specific), % IACS 160 to 180
79

Otherwise Unclassified Properties

Density, g/cm3 2.7
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.4
Stiffness to Weight: Bending, points 50
14
Strength to Weight: Axial, points 13 to 26
6.7 to 11
Strength to Weight: Bending, points 21 to 33
8.5 to 12
Thermal Shock Resistance, points 5.6 to 11
11 to 19

Alloy Composition

Aluminum (Al), % 97.5 to 99
0
Chromium (Cr), % 0 to 0.050
0
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0.15 to 0.35
0
Magnesium (Mg), % 0.6 to 0.9
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0
8.8 to 11
Silicon (Si), % 0.3 to 0.6
0
Silver (Ag), % 0
89 to 91
Titanium (Ti), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.15
0
Residuals, % 0
0 to 0.2