6066-O Aluminum vs. Annealed 90-platinum 10-iridium
6066-O aluminum belongs to the aluminum alloys classification, while annealed 90-platinum 10-iridium belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6066-O aluminum and the bottom bar is annealed 90-platinum 10-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 200 |
| Elongation at Break, % | 17 | |
| 34 |
| Poisson's Ratio | 0.33 | |
| 0.38 |
| Shear Modulus, GPa | 26 | |
| 74 |
| Shear Strength, MPa | 95 | |
| 220 |
| Tensile Strength: Ultimate (UTS), MPa | 160 | |
| 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 100 |
| Melting Completion (Liquidus), °C | 650 | |
| 1830 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 8.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.8 | |
| 22 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 5.3 |
| Stiffness to Weight: Bending, points | 49 | |
| 9.1 |
| Strength to Weight: Axial, points | 16 | |
| 4.2 |
| Strength to Weight: Bending, points | 23 | |
| 4.9 |
| Thermal Shock Resistance, points | 6.9 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 93 to 97 | |
| 0 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 |
| Copper (Cu), % | 0.7 to 1.2 | |
| 0 |
| Iridium (Ir), % | 0 | |
| 9.5 to 10.5 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 |
| Magnesium (Mg), % | 0.8 to 1.4 | |
| 0 |
| Manganese (Mn), % | 0.6 to 1.1 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 89.3 to 90.5 |
| Silicon (Si), % | 0.9 to 1.8 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |