6070 Aluminum vs. 2036 Aluminum
Both 6070 aluminum and 2036 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 6070 aluminum and the bottom bar is 2036 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 70 |
| Elongation at Break, % | 5.6 to 8.6 | |
| 24 |
| Fatigue Strength, MPa | 95 to 130 | |
| 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 220 to 240 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 380 | |
| 340 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 570 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 890 |
| Thermal Conductivity, W/m-K | 160 | |
| 160 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 32 | |
| 70 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 900 | |
| 270 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 48 |
| Strength to Weight: Axial, points | 38 | |
| 33 |
| Strength to Weight: Bending, points | 42 to 43 | |
| 38 |
| Thermal Diffusivity, mm2/s | 65 | |
| 62 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 94.6 to 98 | |
| 94.4 to 97.4 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.15 to 0.4 | |
| 2.2 to 3.0 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.5 to 1.2 | |
| 0.3 to 0.6 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0.1 to 0.4 |
| Silicon (Si), % | 1.0 to 1.7 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |