6082 Aluminum vs. 6014 Aluminum

Both 6082 aluminum and 6014 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 6082 aluminum and the bottom bar is 6014 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
69
Elongation at Break, % 6.3 to 18
9.1 to 17
Fatigue Strength, MPa 55 to 130
43 to 79
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
26
Shear Strength, MPa 84 to 220
96 to 150
Tensile Strength: Ultimate (UTS), MPa 140 to 340
160 to 260
Tensile Strength: Yield (Proof), MPa 85 to 320
80 to 200

Thermal Properties

Latent Heat of Fusion, J/g 410
400
Maximum Temperature: Mechanical, °C 170
180
Melting Completion (Liquidus), °C 650
640
Melting Onset (Solidus), °C 580
620
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 160
200
Thermal Expansion, µm/m-K 23
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
53
Electrical Conductivity: Equal Weight (Specific), % IACS 140
180

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 8.3
8.6
Embodied Energy, MJ/kg 150
160
Embodied Water, L/kg 1170
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 43
22
Resilience: Unit (Modulus of Resilience), kJ/m3 52 to 710
46 to 300
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
50
Strength to Weight: Axial, points 14 to 35
16 to 26
Strength to Weight: Bending, points 21 to 40
24 to 33
Thermal Diffusivity, mm2/s 67
83
Thermal Shock Resistance, points 6.0 to 15
7.0 to 11

Alloy Composition

Aluminum (Al), % 95.2 to 98.3
97.1 to 99.2
Chromium (Cr), % 0 to 0.25
0 to 0.2
Copper (Cu), % 0 to 0.1
0 to 0.25
Iron (Fe), % 0 to 0.5
0 to 0.35
Magnesium (Mg), % 0.6 to 1.2
0.4 to 0.8
Manganese (Mn), % 0.4 to 1.0
0.050 to 0.2
Silicon (Si), % 0.7 to 1.3
0.3 to 0.6
Titanium (Ti), % 0 to 0.1
0 to 0.1
Vanadium (V), % 0
0.050 to 0.2
Zinc (Zn), % 0 to 0.2
0 to 0.1
Residuals, % 0
0 to 0.15

Comparable Variants