60Cr-40Ni Alloy vs. 6110A Aluminum
60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while 6110A aluminum belongs to the aluminum alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is 6110A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 70 |
| Poisson's Ratio | 0.25 | |
| 0.33 |
| Shear Modulus, GPa | 87 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 360 to 470 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 250 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 410 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 900 |
| Thermal Expansion, µm/m-K | 16 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 8.4 |
| Embodied Energy, MJ/kg | 110 | |
| 150 |
| Embodied Water, L/kg | 380 | |
| 1170 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1000 | |
| 450 to 1300 |
| Stiffness to Weight: Axial, points | 16 | |
| 14 |
| Stiffness to Weight: Bending, points | 26 | |
| 50 |
| Strength to Weight: Axial, points | 31 | |
| 36 to 47 |
| Strength to Weight: Bending, points | 26 | |
| 41 to 48 |
| Thermal Shock Resistance, points | 18 | |
| 16 to 21 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 94.8 to 98 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 58 to 62 | |
| 0.050 to 0.25 |
| Copper (Cu), % | 0 | |
| 0.3 to 0.8 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 0.7 to 1.1 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0.3 to 0.9 |
| Nickel (Ni), % | 34.5 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.7 to 1.1 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |