60Cr-40Ni Alloy vs. ACI-ASTM CA15 Steel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while ACI-ASTM CA15 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is ACI-ASTM CA15 steel.

60Cr-40Ni (R20600) Casting Alloy ACI-ASTM CA15 (SCS1, J91150) Cast Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.25
Poisson's Ratio		0.28

Shear Modulus, GPa		87
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		700

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		570

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		280

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		10

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		7.5

Density, g/cm³		7.8
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		2.0

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		28

Embodied Water, L/kg		380
Embodied Water, L/kg		100

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		820

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		25

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		23

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		26

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0 to 0.15

Chromium (Cr), %		58 to 62
Chromium (Cr), %		11.5 to 14

Iron (Fe), %		0 to 1.0
Iron (Fe), %		81.8 to 88.5

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.5

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0 to 1.0

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 1.5

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.040

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0