60Cr-40Ni Alloy vs. ASTM B631 Class C
Both 60Cr-40Ni alloy and ASTM B631 class C are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is ASTM B631 class C.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 180 to 190 |
| Poisson's Ratio | 0.25 | |
| 0.32 |
| Shear Modulus, GPa | 87 | |
| 66 to 71 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 140 to 150 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 180 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 13 to 14 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 55 to 59 |
| Embodied Energy, MJ/kg | 110 | |
| 860 to 920 |
Common Calculations
| Stiffness to Weight: Axial, points | 16 | |
| 7.4 to 7.6 |
| Stiffness to Weight: Bending, points | 26 | |
| 14 |