60Cr-40Ni Alloy vs. EN 1.6579 Steel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while EN 1.6579 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is EN 1.6579 steel.

60Cr-40Ni (R20600) Casting Alloy EN 1.6579 (G35CrNiMo6-6) Cast Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.25
Poisson's Ratio		0.29

Shear Modulus, GPa		87
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		850 to 980

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		600 to 910

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		250

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		3.7

Density, g/cm³		7.8
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		1.7

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		22

Embodied Water, L/kg		380
Embodied Water, L/kg		56

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		950 to 2210

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		30 to 35

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		25 to 28

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		25 to 29

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0.32 to 0.38

Chromium (Cr), %		58 to 62
Chromium (Cr), %		1.4 to 1.7

Iron (Fe), %		0 to 1.0
Iron (Fe), %		94.2 to 96.1

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0.6 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.15 to 0.35

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		1.4 to 1.7

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.6

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.030

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0