60Cr-40Ni Alloy vs. Solder Alloy 123
Both 60Cr-40Ni alloy and solder alloy 123 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is solder alloy 123.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 18 |
| Poisson's Ratio | 0.25 | |
| 0.44 |
| Shear Modulus, GPa | 87 | |
| 6.2 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 28 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 26 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 130 |
| Thermal Expansion, µm/m-K | 16 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 11 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 4.5 |
| Embodied Energy, MJ/kg | 110 | |
| 74 |
| Embodied Water, L/kg | 380 | |
| 500 |
Common Calculations
| Stiffness to Weight: Axial, points | 16 | |
| 0.9 |
| Stiffness to Weight: Bending, points | 26 | |
| 7.8 |
| Strength to Weight: Axial, points | 31 | |
| 0.69 |
| Strength to Weight: Bending, points | 26 | |
| 1.8 |
| Thermal Shock Resistance, points | 18 | |
| 3.8 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 58 to 62 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 93.5 to 95.5 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 34.5 to 42 | |
| 0 to 0.010 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 4.5 to 5.5 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |