60Cr-40Ni Alloy vs. SAE-AISI F1 Steel
60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while SAE-AISI F1 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is SAE-AISI F1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Poisson's Ratio | 0.25 | |
| 0.29 |
| Shear Modulus, GPa | 87 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 620 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 5.0 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 1.7 |
| Embodied Energy, MJ/kg | 110 | |
| 24 |
| Embodied Water, L/kg | 380 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 16 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 22 to 82 |
| Strength to Weight: Bending, points | 26 | |
| 20 to 49 |
| Thermal Shock Resistance, points | 18 | |
| 19 to 70 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 1.0 to 1.3 |
| Chromium (Cr), % | 58 to 62 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 95.9 to 98 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 to 0.5 |
| Nickel (Ni), % | 34.5 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 1.0 to 1.8 |