60Cr-40Ni Alloy vs. SAE-AISI H42 Steel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while SAE-AISI H42 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is SAE-AISI H42 steel.

60Cr-40Ni (R20600) Casting Alloy SAE-AISI H42 (T20842) Molybdenum Hot-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.25
Poisson's Ratio		0.29

Shear Modulus, GPa		87
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		700 to 1980

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		24

Density, g/cm³		7.8
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		8.8

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		130

Embodied Water, L/kg		380
Embodied Water, L/kg		98

Common Calculations

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		23 to 65

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		21 to 42

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		20 to 57

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0.55 to 0.7

Chromium (Cr), %		58 to 62
Chromium (Cr), %		3.8 to 4.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 1.0
Iron (Fe), %		79.3 to 83.8

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		4.5 to 5.5

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0 to 0.3

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.030

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0

Tungsten (W), %		0
Tungsten (W), %		5.5 to 6.8

Vanadium (V), %		0
Vanadium (V), %		1.8 to 2.2