60Cr-40Ni Alloy vs. C17000 Copper

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while C17000 copper belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is C17000 copper.

60Cr-40Ni (R20600) Casting Alloy UNS C17000 (CW100C) Beryllium Copper

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.25
Poisson's Ratio		0.33

Shear Modulus, GPa		87
Shear Modulus, GPa		45

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		490 to 1310

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		160 to 1140

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		230

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Density, g/cm³		7.8
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		8.7

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		140

Embodied Water, L/kg		380
Embodied Water, L/kg		310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		110 to 5420

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		7.6

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		15 to 41

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		16 to 30

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		17 to 45

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0 to 0.2

Beryllium (Be), %		0
Beryllium (Be), %		1.6 to 1.8

Carbon (C), %		0 to 0.1
Carbon (C), %		0

Chromium (Cr), %		58 to 62
Chromium (Cr), %		0

Copper (Cu), %		0
Copper (Cu), %		96.3 to 98.2

Iron (Fe), %		0 to 1.0
Iron (Fe), %		0 to 0.4

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0.2 to 0.6

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.2

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0

Residuals, %		0
Residuals, %		0 to 0.5