60Cr-40Ni Alloy vs. C18600 Copper

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while C18600 copper belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is C18600 copper.

60Cr-40Ni (R20600) Casting Alloy UNS C18600 Chromium Copper

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.25
Poisson's Ratio		0.34

Shear Modulus, GPa		87
Shear Modulus, GPa		44

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		520 to 580

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		500 to 520

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		210

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		31

Density, g/cm³		7.8
Density, g/cm³		8.9

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		2.9

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		46

Embodied Water, L/kg		380
Embodied Water, L/kg		310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		1060 to 1180

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		7.3

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		18

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		16 to 18

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		16 to 17

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		19 to 20

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0

Chromium (Cr), %		58 to 62
Chromium (Cr), %		0.1 to 1.0

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.1

Copper (Cu), %		0
Copper (Cu), %		96.5 to 99.55

Iron (Fe), %		0 to 1.0
Iron (Fe), %		0.25 to 0.8

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0 to 0.25

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0.050 to 0.5

Zirconium (Zr), %		0
Zirconium (Zr), %		0.050 to 0.4

Residuals, %		0
Residuals, %		0 to 0.5