60Cr-40Ni Alloy vs. C19000 Copper

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while C19000 copper belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is C19000 copper.

60Cr-40Ni (R20600) Casting Alloy UNS C19000 (CW108C) Nickel-Phosphorus Copper

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.25
Poisson's Ratio		0.34

Shear Modulus, GPa		87
Shear Modulus, GPa		43

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		260 to 760

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		140 to 630

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		210

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		31

Density, g/cm³		7.8
Density, g/cm³		8.9

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		42

Embodied Water, L/kg		380
Embodied Water, L/kg		310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		89 to 1730

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		7.2

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		18

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		8.2 to 24

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		10 to 21

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		9.3 to 27

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0

Chromium (Cr), %		58 to 62
Chromium (Cr), %		0

Copper (Cu), %		0
Copper (Cu), %		96.9 to 99

Iron (Fe), %		0 to 1.0
Iron (Fe), %		0 to 0.1

Lead (Pb), %		0
Lead (Pb), %		0 to 0.050

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0.9 to 1.3

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0.15 to 0.35

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.8

Residuals, %		0
Residuals, %		0 to 0.5