60Cr-40Ni Alloy vs. C63000 Bronze

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while C63000 bronze belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is C63000 bronze.

60Cr-40Ni (R20600) Casting Alloy UNS C63000 (CW307G) Aluminum-Nickel Bronze

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.25
Poisson's Ratio		0.34

Shear Modulus, GPa		87
Shear Modulus, GPa		44

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		660 to 790

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		330 to 390

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		230

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		18

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		29

Density, g/cm³		7.8
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		3.5

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		57

Embodied Water, L/kg		380
Embodied Water, L/kg		390

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		470 to 640

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		7.9

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		20

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		22 to 26

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		20 to 23

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		23 to 27

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		9.0 to 11

Carbon (C), %		0 to 0.1
Carbon (C), %		0

Chromium (Cr), %		58 to 62
Chromium (Cr), %		0

Copper (Cu), %		0
Copper (Cu), %		76.8 to 85

Iron (Fe), %		0 to 1.0
Iron (Fe), %		2.0 to 4.0

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0 to 1.5

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		4.0 to 5.5

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.25

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		0 to 0.2

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.3

Residuals, %		0
Residuals, %		0 to 0.5