60Cr-40Ni Alloy vs. C97600 Dairy Metal
60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while C97600 dairy metal belongs to the copper alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is C97600 dairy metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Poisson's Ratio | 0.25 | |
| 0.33 |
| Shear Modulus, GPa | 87 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 310 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 380 |
| Thermal Expansion, µm/m-K | 16 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 37 |
| Density, g/cm3 | 7.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 4.6 |
| Embodied Energy, MJ/kg | 110 | |
| 69 |
| Embodied Water, L/kg | 380 | |
| 330 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1000 | |
| 85 |
| Stiffness to Weight: Axial, points | 16 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 26 | |
| 19 |
| Strength to Weight: Axial, points | 31 | |
| 9.8 |
| Strength to Weight: Bending, points | 26 | |
| 12 |
| Thermal Shock Resistance, points | 18 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 58 to 62 | |
| 0 |
| Copper (Cu), % | 0 | |
| 63 to 67 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 1.5 |
| Lead (Pb), % | 0 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 34.5 to 42 | |
| 19 to 21.5 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 3.5 to 4.0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 3.0 to 9.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |