6101A Aluminum vs. 1435 Aluminum
Both 6101A aluminum and 1435 aluminum are aluminum alloys. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is 6101A aluminum and the bottom bar is 1435 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 69 |
| Elongation at Break, % | 11 | |
| 4.1 to 32 |
| Fatigue Strength, MPa | 80 | |
| 27 to 49 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 130 | |
| 54 to 87 |
| Tensile Strength: Ultimate (UTS), MPa | 220 | |
| 81 to 150 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 23 to 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 630 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 200 | |
| 230 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 55 | |
| 60 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 200 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.0 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 | |
| 5.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
| 3.8 to 110 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 23 | |
| 8.3 to 15 |
| Strength to Weight: Bending, points | 30 | |
| 15 to 23 |
| Thermal Diffusivity, mm2/s | 84 | |
| 93 |
| Thermal Shock Resistance, points | 10 | |
| 3.6 to 6.7 |
Alloy Composition
| Aluminum (Al), % | 97.9 to 99.3 | |
| 99.35 to 99.7 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.4 | |
| 0.3 to 0.5 |
| Magnesium (Mg), % | 0.4 to 0.9 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0.3 to 0.7 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.1 | |
| 0 |