6101B Aluminum vs. 6182 Aluminum
Both 6101B aluminum and 6182 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 6101B aluminum and the bottom bar is 6182 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 70 |
| Elongation at Break, % | 9.1 to 13 | |
| 6.8 to 13 |
| Fatigue Strength, MPa | 62 to 70 | |
| 63 to 99 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 120 to 150 | |
| 140 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 250 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 140 to 180 | |
| 130 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 630 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 210 | |
| 160 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 57 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.4 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 23 | |
| 21 to 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 240 | |
| 110 to 520 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 20 to 25 | |
| 23 to 32 |
| Strength to Weight: Bending, points | 27 to 32 | |
| 30 to 38 |
| Thermal Diffusivity, mm2/s | 87 | |
| 65 |
| Thermal Shock Resistance, points | 8.5 to 11 | |
| 10 to 14 |
Alloy Composition
| Aluminum (Al), % | 98.2 to 99.3 | |
| 95 to 97.9 |
| Chromium (Cr), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.1 |
| Iron (Fe), % | 0.1 to 0.3 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.35 to 0.6 | |
| 0.7 to 1.2 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0.5 to 1.0 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0.9 to 1.3 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 0 | |
| 0.050 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |