6101B Aluminum vs. EN 1.3537 Steel

6101B aluminum belongs to the aluminum alloys classification, while EN 1.3537 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6101B aluminum and the bottom bar is EN 1.3537 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 190 to 250
620 to 730

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 160
440
Melting Completion (Liquidus), °C 640
1450
Melting Onset (Solidus), °C 630
1410
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 210
43
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 57
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 190
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.8
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.3
1.5
Embodied Energy, MJ/kg 150
21
Embodied Water, L/kg 1190
54

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 20 to 25
22 to 26
Strength to Weight: Bending, points 27 to 32
21 to 23
Thermal Diffusivity, mm2/s 87
12
Thermal Shock Resistance, points 8.5 to 11
18 to 22

Alloy Composition

Aluminum (Al), % 98.2 to 99.3
0 to 0.050
Carbon (C), % 0
0.93 to 1.1
Chromium (Cr), % 0
1.7 to 2.0
Copper (Cu), % 0 to 0.050
0 to 0.3
Iron (Fe), % 0.1 to 0.3
96.4 to 97.8
Magnesium (Mg), % 0.35 to 0.6
0
Manganese (Mn), % 0 to 0.050
0.25 to 0.45
Molybdenum (Mo), % 0
0.15 to 0.3
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.3 to 0.6
0.15 to 0.45
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.1
0