6110A Aluminum vs. 7020 Aluminum
Both 6110A aluminum and 7020 aluminum are aluminum alloys. They have a very high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6110A aluminum and the bottom bar is 7020 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 70 |
| Elongation at Break, % | 11 to 18 | |
| 8.4 to 14 |
| Fatigue Strength, MPa | 140 to 210 | |
| 110 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 220 to 280 | |
| 110 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 470 | |
| 190 to 390 |
| Tensile Strength: Yield (Proof), MPa | 250 to 430 | |
| 120 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 210 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 600 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Conductivity, W/m-K | 160 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 42 | |
| 39 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 58 | |
| 23 to 46 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 to 1300 | |
| 110 to 690 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 47 |
| Strength to Weight: Axial, points | 36 to 47 | |
| 18 to 37 |
| Strength to Weight: Bending, points | 41 to 48 | |
| 25 to 41 |
| Thermal Diffusivity, mm2/s | 65 | |
| 59 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 8.3 to 17 |
Alloy Composition
| Aluminum (Al), % | 94.8 to 98 | |
| 91.2 to 94.8 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 0.1 to 0.35 |
| Copper (Cu), % | 0.3 to 0.8 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.7 to 1.1 | |
| 1.0 to 1.4 |
| Manganese (Mn), % | 0.3 to 0.9 | |
| 0.050 to 0.5 |
| Silicon (Si), % | 0.7 to 1.1 | |
| 0 to 0.35 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.2 | |
| 4.0 to 5.0 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0.080 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |