6110A Aluminum vs. EN 1.1118 Cast Steel

6110A aluminum belongs to the aluminum alloys classification, while EN 1.1118 cast steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110A aluminum and the bottom bar is EN 1.1118 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
190
Elongation at Break, % 11 to 18
14 to 21
Fatigue Strength, MPa 140 to 210
320 to 400
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 360 to 470
700 to 750
Tensile Strength: Yield (Proof), MPa 250 to 430
460 to 630

Thermal Properties

Latent Heat of Fusion, J/g 410
250
Maximum Temperature: Mechanical, °C 190
400
Melting Completion (Liquidus), °C 650
1460
Melting Onset (Solidus), °C 600
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 160
51
Thermal Expansion, µm/m-K 23
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 140
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
1.9
Density, g/cm3 2.8
7.8
Embodied Carbon, kg CO2/kg material 8.4
1.4
Embodied Energy, MJ/kg 150
19
Embodied Water, L/kg 1170
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 47 to 58
97 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 450 to 1300
550 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 36 to 47
25 to 27
Strength to Weight: Bending, points 41 to 48
22 to 23
Thermal Diffusivity, mm2/s 65
14
Thermal Shock Resistance, points 16 to 21
22 to 24

Alloy Composition

Aluminum (Al), % 94.8 to 98
0
Carbon (C), % 0
0.2 to 0.25
Chromium (Cr), % 0.050 to 0.25
0
Copper (Cu), % 0.3 to 0.8
0
Iron (Fe), % 0 to 0.5
97.3 to 98.3
Magnesium (Mg), % 0.7 to 1.1
0
Manganese (Mn), % 0.3 to 0.9
1.5 to 1.8
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0.7 to 1.1
0 to 0.6
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0 to 0.2
0
Residuals, % 0 to 0.15
0