6162 Aluminum vs. 5052 Aluminum
Both 6162 aluminum and 5052 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 6162 aluminum and the bottom bar is 5052 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 6.7 to 9.1 | |
| 1.1 to 22 |
| Fatigue Strength, MPa | 100 to 130 | |
| 66 to 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 170 to 180 | |
| 120 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 300 | |
| 190 to 320 |
| Tensile Strength: Yield (Proof), MPa | 260 to 270 | |
| 75 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 620 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 190 | |
| 140 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 170 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 26 | |
| 1.7 to 69 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 550 | |
| 41 to 590 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 29 to 30 | |
| 19 to 33 |
| Strength to Weight: Bending, points | 36 | |
| 27 to 38 |
| Thermal Diffusivity, mm2/s | 79 | |
| 57 |
| Thermal Shock Resistance, points | 13 | |
| 8.3 to 14 |
Alloy Composition
| Aluminum (Al), % | 96.7 to 98.9 | |
| 95.8 to 97.7 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.7 to 1.1 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Silicon (Si), % | 0.4 to 0.8 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |