6182 Aluminum vs. 5652 Aluminum
Both 6182 aluminum and 5652 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6182 aluminum and the bottom bar is 5652 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 6.8 to 13 | |
| 6.8 to 25 |
| Fatigue Strength, MPa | 63 to 99 | |
| 60 to 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 140 to 190 | |
| 110 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 190 to 290 |
| Tensile Strength: Yield (Proof), MPa | 130 to 270 | |
| 74 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 600 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 160 | |
| 140 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 26 | |
| 12 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 520 | |
| 40 to 480 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 51 |
| Strength to Weight: Axial, points | 23 to 32 | |
| 20 to 30 |
| Strength to Weight: Bending, points | 30 to 38 | |
| 27 to 36 |
| Thermal Diffusivity, mm2/s | 65 | |
| 57 |
| Thermal Shock Resistance, points | 10 to 14 | |
| 8.4 to 13 |
Alloy Composition
| Aluminum (Al), % | 95 to 97.9 | |
| 95.8 to 97.7 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.040 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.7 to 1.2 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0.9 to 1.3 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0.050 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |