6182 Aluminum vs. 6014 Aluminum
Both 6182 aluminum and 6014 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 6182 aluminum and the bottom bar is 6014 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 69 |
| Elongation at Break, % | 6.8 to 13 | |
| 9.1 to 17 |
| Fatigue Strength, MPa | 63 to 99 | |
| 43 to 79 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 140 to 190 | |
| 96 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 160 to 260 |
| Tensile Strength: Yield (Proof), MPa | 130 to 270 | |
| 80 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 600 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 160 | |
| 200 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 53 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1170 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 26 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 520 | |
| 46 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 23 to 32 | |
| 16 to 26 |
| Strength to Weight: Bending, points | 30 to 38 | |
| 24 to 33 |
| Thermal Diffusivity, mm2/s | 65 | |
| 83 |
| Thermal Shock Resistance, points | 10 to 14 | |
| 7.0 to 11 |
Alloy Composition
| Aluminum (Al), % | 95 to 97.9 | |
| 97.1 to 99.2 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0.7 to 1.2 | |
| 0.4 to 0.8 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0.050 to 0.2 |
| Silicon (Si), % | 0.9 to 1.3 | |
| 0.3 to 0.6 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.2 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0.050 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |