6261 Aluminum vs. AWS BMg-1
6261 aluminum belongs to the aluminum alloys classification, while AWS BMg-1 belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6261 aluminum and the bottom bar is AWS BMg-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 47 |
| Elongation at Break, % | 9.0 to 16 | |
| 3.8 |
| Fatigue Strength, MPa | 60 to 120 | |
| 72 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 90 to 180 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 300 | |
| 180 |
| Tensile Strength: Yield (Proof), MPa | 100 to 260 | |
| 110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 640 | |
| 600 |
| Melting Onset (Solidus), °C | 610 | |
| 440 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 980 |
| Thermal Conductivity, W/m-K | 180 | |
| 76 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 48 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 160 | |
| 55 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.8 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 22 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 27 | |
| 5.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 77 to 500 | |
| 120 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 66 |
| Strength to Weight: Axial, points | 15 to 31 | |
| 27 |
| Strength to Weight: Bending, points | 23 to 37 | |
| 39 |
| Thermal Diffusivity, mm2/s | 75 | |
| 43 |
| Thermal Shock Resistance, points | 6.5 to 13 | |
| 10 |
Alloy Composition
| Aluminum (Al), % | 96.6 to 98.6 | |
| 8.3 to 9.7 |
| Beryllium (Be), % | 0 | |
| 0.00020 to 0.00080 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0.15 to 0.4 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0.7 to 1.0 | |
| 86.1 to 89.8 |
| Manganese (Mn), % | 0.2 to 0.35 | |
| 0.15 to 1.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0.4 to 0.7 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 1.7 to 2.3 |
| Residuals, % | 0 | |
| 0 to 0.3 |