6261 Aluminum vs. EN 1.3563 Steel

6261 aluminum belongs to the aluminum alloys classification, while EN 1.3563 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6261 aluminum and the bottom bar is EN 1.3563 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 150 to 300
690 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 160
420
Melting Completion (Liquidus), °C 640
1460
Melting Onset (Solidus), °C 610
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 180
43
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 48
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 160
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.5
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.3
1.5
Embodied Energy, MJ/kg 150
20
Embodied Water, L/kg 1180
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 15 to 31
24 to 65
Strength to Weight: Bending, points 23 to 37
22 to 43
Thermal Diffusivity, mm2/s 75
12
Thermal Shock Resistance, points 6.5 to 13
20 to 54

Alloy Composition

Aluminum (Al), % 96.6 to 98.6
0 to 0.050
Carbon (C), % 0
0.4 to 0.46
Chromium (Cr), % 0 to 0.1
0.9 to 1.2
Copper (Cu), % 0.15 to 0.4
0 to 0.3
Iron (Fe), % 0 to 0.4
96.8 to 98.4
Magnesium (Mg), % 0.7 to 1.0
0
Manganese (Mn), % 0.2 to 0.35
0.6 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.3
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.4 to 0.7
0 to 0.4
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.15
0

Comparable Variants