6463 Aluminum vs. K93600 Alloy
6463 aluminum belongs to the aluminum alloys classification, while K93600 alloy belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6463 aluminum and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 140 |
| Elongation at Break, % | 9.0 to 17 | |
| 5.0 to 35 |
| Shear Strength, MPa | 86 to 150 | |
| 320 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 230 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 82 to 200 | |
| 280 to 750 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 160 | |
| 440 |
| Melting Onset (Solidus), °C | 620 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 520 |
| Thermal Conductivity, W/m-K | 190 to 210 | |
| 13 |
| Thermal Expansion, µm/m-K | 23 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 to 55 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 170 to 180 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 25 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 50 to 300 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 14 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 50 | |
| 21 |
| Strength to Weight: Axial, points | 14 to 24 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 22 to 31 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 79 to 86 | |
| 3.1 |
| Thermal Shock Resistance, points | 6.3 to 10 | |
| 34 to 57 |