70Ag-30Ni Alloy vs. 711.0 Aluminum

70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while 711.0 aluminum belongs to the aluminum alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is 711.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
71
Poisson's Ratio 0.35
0.32
Shear Modulus, GPa 39
27
Tensile Strength: Ultimate (UTS), MPa 320 to 530
220

Thermal Properties

Latent Heat of Fusion, J/g 170
380
Melting Completion (Liquidus), °C 960
640
Melting Onset (Solidus), °C 960
610
Specific Heat Capacity, J/kg-K 300
860
Thermal Expansion, µm/m-K 17
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 69
40
Electrical Conductivity: Equal Weight (Specific), % IACS 62
120

Otherwise Unclassified Properties

Density, g/cm3 10
3.0

Common Calculations

Stiffness to Weight: Axial, points 5.8
13
Stiffness to Weight: Bending, points 16
45
Strength to Weight: Axial, points 8.8 to 15
20
Strength to Weight: Bending, points 10 to 15
26
Thermal Shock Resistance, points 13 to 21
9.3

Alloy Composition

Aluminum (Al), % 0
89.8 to 92.7
Copper (Cu), % 0
0.35 to 0.65
Iron (Fe), % 0
0.7 to 1.4
Magnesium (Mg), % 0
0.25 to 0.45
Manganese (Mn), % 0
0 to 0.050
Nickel (Ni), % 28.8 to 31
0
Silicon (Si), % 0
0 to 0.3
Silver (Ag), % 69 to 71
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
6.0 to 7.0
Residuals, % 0
0 to 0.15