70Ag-30Ni Alloy vs. EN 1.3555 Steel

70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while EN 1.3555 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is EN 1.3555 steel.

70-Silver 30-Nickel Electrical Contact Alloy EN 1.3555 (13MoCrNi42-16-14) High-Temperature Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		100
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.35
Poisson's Ratio		0.29

Shear Modulus, GPa		39
Shear Modulus, GPa		75

Tensile Strength: Ultimate (UTS), MPa		320 to 530
Tensile Strength: Ultimate (UTS), MPa		770

Thermal Properties

Latent Heat of Fusion, J/g		170
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		960
Melting Completion (Liquidus), °C		1500

Melting Onset (Solidus), °C		960
Melting Onset (Solidus), °C		1450

Specific Heat Capacity, J/kg-K		300
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		69
Electrical Conductivity: Equal Volume, % IACS		9.3

Electrical Conductivity: Equal Weight (Specific), % IACS		62
Electrical Conductivity: Equal Weight (Specific), % IACS		11

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.9

Common Calculations

Stiffness to Weight: Axial, points		5.8
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		16
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		8.8 to 15
Strength to Weight: Axial, points		27

Strength to Weight: Bending, points		10 to 15
Strength to Weight: Bending, points		23

Thermal Shock Resistance, points		13 to 21
Thermal Shock Resistance, points		22

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0.1 to 0.15

Chromium (Cr), %		0
Chromium (Cr), %		3.9 to 4.3

Copper (Cu), %		0
Copper (Cu), %		0 to 0.1

Iron (Fe), %		0
Iron (Fe), %		85.4 to 87.7

Manganese (Mn), %		0
Manganese (Mn), %		0.15 to 0.35

Molybdenum (Mo), %		0
Molybdenum (Mo), %		4.0 to 4.5

Nickel (Ni), %		28.8 to 31
Nickel (Ni), %		3.2 to 3.6

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.015

Silicon (Si), %		0
Silicon (Si), %		0.1 to 0.25

Silver (Ag), %		69 to 71
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.010

Tungsten (W), %		0
Tungsten (W), %		0 to 0.15

Vanadium (V), %		0
Vanadium (V), %		1.0 to 1.3

Residuals, %		0 to 0.2
Residuals, %		0