70Ag-30Ni Alloy vs. EN 1.4568 Stainless Steel
70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while EN 1.4568 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is EN 1.4568 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Poisson's Ratio | 0.35 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 530 | |
| 830 to 1620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Melting Completion (Liquidus), °C | 960 | |
| 1420 |
| Melting Onset (Solidus), °C | 960 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 69 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 | |
| 2.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 16 | |
| 25 |
| Strength to Weight: Axial, points | 8.8 to 15 | |
| 30 to 58 |
| Strength to Weight: Bending, points | 10 to 15 | |
| 25 to 40 |
| Thermal Shock Resistance, points | 13 to 21 | |
| 23 to 46 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.7 to 1.5 |
| Carbon (C), % | 0 | |
| 0 to 0.090 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Iron (Fe), % | 0 | |
| 70.9 to 76.8 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 28.8 to 31 | |
| 6.5 to 7.8 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Silver (Ag), % | 69 to 71 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Residuals, % | 0 to 0.2 | |
| 0 |