70Ag-30Ni Alloy vs. CC382H Copper-nickel

70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while CC382H copper-nickel belongs to the copper alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is CC382H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
140
Poisson's Ratio 0.35
0.33
Shear Modulus, GPa 39
53
Tensile Strength: Ultimate (UTS), MPa 320 to 530
490

Thermal Properties

Latent Heat of Fusion, J/g 170
240
Melting Completion (Liquidus), °C 960
1180
Melting Onset (Solidus), °C 960
1120
Specific Heat Capacity, J/kg-K 300
410
Thermal Expansion, µm/m-K 17
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 69
5.5
Electrical Conductivity: Equal Weight (Specific), % IACS 62
5.6

Otherwise Unclassified Properties

Density, g/cm3 10
8.9

Common Calculations

Stiffness to Weight: Axial, points 5.8
8.8
Stiffness to Weight: Bending, points 16
20
Strength to Weight: Axial, points 8.8 to 15
15
Strength to Weight: Bending, points 10 to 15
16
Thermal Shock Resistance, points 13 to 21
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Bismuth (Bi), % 0
0 to 0.0020
Boron (B), % 0
0 to 0.010
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
1.5 to 2.0
Copper (Cu), % 0
62.8 to 68.4
Iron (Fe), % 0
0.5 to 1.0
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 0
0 to 0.010
Manganese (Mn), % 0
0.5 to 1.0
Nickel (Ni), % 28.8 to 31
29 to 32
Phosphorus (P), % 0
0 to 0.010
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0
0.15 to 0.5
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.010
Tellurium (Te), % 0
0 to 0.0050
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.2
Zirconium (Zr), % 0
0 to 0.15
Residuals, % 0 to 0.2
0