70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while C94700 bronze belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is C94700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
110
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 39
43
Tensile Strength: Ultimate (UTS), MPa 320 to 530
350 to 590

Thermal Properties

Latent Heat of Fusion, J/g 170
200
Melting Completion (Liquidus), °C 960
1030
Melting Onset (Solidus), °C 960
900
Specific Heat Capacity, J/kg-K 300
380
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 69
12
Electrical Conductivity: Equal Weight (Specific), % IACS 62
12

Otherwise Unclassified Properties

Density, g/cm3 10
8.8

Common Calculations

Stiffness to Weight: Axial, points 5.8
7.3
Stiffness to Weight: Bending, points 16
18
Strength to Weight: Axial, points 8.8 to 15
11 to 19
Strength to Weight: Bending, points 10 to 15
13 to 18
Thermal Shock Resistance, points 13 to 21
12 to 21

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.15
Copper (Cu), % 0
85 to 90
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0
0 to 0.2
Nickel (Ni), % 28.8 to 31
4.5 to 6.0
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
4.5 to 6.0
Zinc (Zn), % 0
1.0 to 2.5
Residuals, % 0
0 to 1.3