70Ag-30Ni Alloy vs. R58150 Titanium
70Ag-30Ni alloy belongs to the otherwise unclassified metals classification, while R58150 titanium belongs to the titanium alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is 70Ag-30Ni alloy and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 140 |
| Poisson's Ratio | 0.35 | |
| 0.32 |
| Shear Modulus, GPa | 39 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 530 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 410 |
| Melting Completion (Liquidus), °C | 960 | |
| 1760 |
| Melting Onset (Solidus), °C | 960 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 500 |
| Thermal Expansion, µm/m-K | 17 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 5.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 16 | |
| 32 |
| Strength to Weight: Axial, points | 8.8 to 15 | |
| 40 |
| Strength to Weight: Bending, points | 10 to 15 | |
| 35 |
| Thermal Shock Resistance, points | 13 to 21 | |
| 48 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 14 to 16 |
| Nickel (Ni), % | 28.8 to 31 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silver (Ag), % | 69 to 71 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 83.5 to 86 |
| Residuals, % | 0 to 0.2 | |
| 0 |