7005 Aluminum vs. 6162 Aluminum
Both 7005 aluminum and 6162 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 7005 aluminum and the bottom bar is 6162 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 10 to 20 | |
| 6.7 to 9.1 |
| Fatigue Strength, MPa | 100 to 190 | |
| 100 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 120 to 230 | |
| 170 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 400 | |
| 290 to 300 |
| Tensile Strength: Yield (Proof), MPa | 95 to 350 | |
| 260 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 to 170 | |
| 190 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 to 43 | |
| 50 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 to 130 | |
| 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 32 to 57 | |
| 19 to 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 850 | |
| 510 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 50 |
| Strength to Weight: Axial, points | 19 to 38 | |
| 29 to 30 |
| Strength to Weight: Bending, points | 26 to 41 | |
| 36 |
| Thermal Diffusivity, mm2/s | 54 to 65 | |
| 79 |
| Thermal Shock Resistance, points | 8.7 to 18 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 91 to 94.7 | |
| 96.7 to 98.9 |
| Chromium (Cr), % | 0.060 to 0.2 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 1.0 to 1.8 | |
| 0.7 to 1.1 |
| Manganese (Mn), % | 0.2 to 0.7 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.35 | |
| 0.4 to 0.8 |
| Titanium (Ti), % | 0.010 to 0.060 | |
| 0 to 0.1 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0.080 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |