7005 Aluminum vs. R31538 Cobalt
7005 aluminum belongs to the aluminum alloys classification, while R31538 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 7005 aluminum and the bottom bar is R31538 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 220 |
| Elongation at Break, % | 10 to 20 | |
| 13 to 23 |
| Fatigue Strength, MPa | 100 to 190 | |
| 310 to 480 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 400 | |
| 1020 to 1360 |
| Tensile Strength: Yield (Proof), MPa | 95 to 350 | |
| 580 to 930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 320 |
| Melting Completion (Liquidus), °C | 640 | |
| 1360 |
| Melting Onset (Solidus), °C | 610 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 450 |
| Thermal Conductivity, W/m-K | 140 to 170 | |
| 13 |
| Thermal Expansion, µm/m-K | 23 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 to 43 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 to 130 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 110 |
| Embodied Water, L/kg | 1150 | |
| 530 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 32 to 57 | |
| 140 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 850 | |
| 750 to 1920 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 47 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 38 | |
| 34 to 45 |
| Strength to Weight: Bending, points | 26 to 41 | |
| 27 to 32 |
| Thermal Diffusivity, mm2/s | 54 to 65 | |
| 3.5 |
| Thermal Shock Resistance, points | 8.7 to 18 | |
| 25 to 33 |
Alloy Composition
| Aluminum (Al), % | 91 to 94.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.15 to 0.35 |
| Chromium (Cr), % | 0.060 to 0.2 | |
| 26 to 30 |
| Cobalt (Co), % | 0 | |
| 58.7 to 68.9 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.75 |
| Magnesium (Mg), % | 1.0 to 1.8 | |
| 0 |
| Manganese (Mn), % | 0.2 to 0.7 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.0 |
| Titanium (Ti), % | 0.010 to 0.060 | |
| 0 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 |
| Zirconium (Zr), % | 0.080 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |