7010 Aluminum vs. 5449 Aluminum
Both 7010 aluminum and 5449 aluminum are aluminum alloys. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is 7010 aluminum and the bottom bar is 5449 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 69 |
| Elongation at Break, % | 3.9 to 6.8 | |
| 4.0 to 17 |
| Fatigue Strength, MPa | 160 to 190 | |
| 78 to 120 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 300 to 340 | |
| 130 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 590 | |
| 210 to 330 |
| Tensile Strength: Yield (Proof), MPa | 410 to 540 | |
| 91 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 190 |
| Melting Completion (Liquidus), °C | 630 | |
| 650 |
| Melting Onset (Solidus), °C | 480 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 900 |
| Thermal Conductivity, W/m-K | 150 | |
| 140 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.5 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1120 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 22 to 33 | |
| 12 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1230 to 2130 | |
| 60 to 480 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 50 |
| Strength to Weight: Axial, points | 47 to 54 | |
| 22 to 33 |
| Strength to Weight: Bending, points | 47 to 52 | |
| 29 to 39 |
| Thermal Diffusivity, mm2/s | 58 | |
| 56 |
| Thermal Shock Resistance, points | 22 to 26 | |
| 9.4 to 15 |
Alloy Composition
| Aluminum (Al), % | 87.9 to 90.6 | |
| 94.1 to 97.8 |
| Chromium (Cr), % | 0 to 0.050 | |
| 0 to 0.3 |
| Copper (Cu), % | 1.5 to 2.0 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 2.1 to 2.6 | |
| 1.6 to 2.6 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.6 to 1.1 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.12 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.060 | |
| 0 to 0.1 |
| Zinc (Zn), % | 5.7 to 6.7 | |
| 0 to 0.3 |
| Zirconium (Zr), % | 0.1 to 0.16 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |